福建兴业钢管有限公司

O.D: 17.1mm Seamless Steel Tubes

Home / Products / Seamless Steel Tubes

Bright tube
Pickling tube

O.D: 17.1mm Seamless Steel Tubes

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:1.65mm - 3.20mm

Bright tube
Pickling tube

MIN - 0.8mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:0.8mm

Bright tube
Pickling tube

SCH10s - 1.65mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:1.65mm

Bright tube
Pickling tube

SCH40s - 2.31mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:2.31mm

Bright tube
Pickling tube

STD - 2.31mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:2.31mm

Bright tube
Pickling tube

SCH40 - 2.31mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:2.31mm

Bright tube
Pickling tube

SCH80s - 3.20mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:3.20mm

Bright tube
Pickling tube

XS - 3.20mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:3.20mm

Bright tube
Pickling tube

SCH80 - 3.20mm

American Standard ANSI B36.10 / B36.19M

MIN:0.8mm
BN:10
O.D:17.1mm
NPS:3/8
W.T:3.20mm

Stainless steel pipe:

MIN:0.8mm
SCH10s: 1.65mm
SCH40s: 2.31mm
STD: 2.31mm
SCH40: 2.31mm
SCH80s: 3.20mm
XS: 3.20mm
SCH80: 3.20mm

Product Description:

It is a precipitation hardening type of high strength stainless steel. It has excellent corrosion resistance equivalent to that of austenitic stainless steels, and also provides high strength equivalent to chromium stainless steels which have a quench-hardening capacity.

• Outside Diameter17.1mm
• Circular hollow sections up to 1.65mm - 3.20mm

Advantages of Seamless Steel Tubes:

• Excellent formability
• Good weldability
• Excellent corrosion resistance
• Fire resistance
• Toughness at low temperatures

Product Specifications:

NORMINAL PIPE SIZE		OUTSIDE DIAMETER		NORMINAL WALL THICKNESS		TECHNOLOGY
NPS	BN	D		MIN		SURFACE TREATMENT
3/8	10	17.1mm		0.8		Pickling

Heat Treatment	It is normally supplied in a solution-treated condition. However, in order to obtain the maximum mechanical properties, it is necessary to perform H900 precipitation hardening heat treatment after working. If ductility is required, we recommend using H1150 precipitation hardening heat treatment. In this case, it is possible to perform precipitation hardening heat treatment of the base material, as working is also possible after precipitation hardening. Heat treatment conditions • H900 precipitation hardening: 470~490℃; air cooling • H1150 precipitation hardening: 610~630℃; air cooling
Weldability	Excellent weldability. By various welding methods. The maximum welding efficiency can be obtained by conventional treatment after welding.
Pickling	In pickling of comparatively thick scale after solution treatment or hot working, the methods used with austenitic stainless steels can be used.
Applications	General purpose stainless steel. Provides excellent performance balance while being easy to use. Food equipment, general chemicals, daily necessities.